The intermediary outside occupying reports, institute of data of Japanese national material (NationalInstituteforMaterialsScience, the research group of NIMS) and university of science of national technology length ridge (NagaokaUniversityofTechnology) joint research and development magnesium alloy of new fund high strenth board (Mg–1.1Al–0.3Ca–0.2Mn–0.3Zn) .
relatively at certain car look forward to gold of Ban of present automobile body uses aluminous metal is laminose (Aluminumsheetmetal) , below its normal temperature shape performance is quite excellent. After classics heat treatment, the intensity of this magnesium alloy is higher than aluminium alloy, its use common metallic data only, what did not come or will make a low cost is light quantify a car to use sheet metal.
A long time ago, light quantified magnesium alloy pays close attention to with respect to what already caused automobile industry, numerous car look forward to hopes to use this data in application of of all kinds car. However, because magnesium alloy issues intensity in room temperature low, shape performance is poor, block up the applied promotion of alloy of magnesium board shape. Normally, extend shape ability (Stretchformability) and succumb intensity (Yieldstrength) presents converse dependency. For this, ensure high strenth is reached very hard at the same time tall shape function.
But recent research makes clear, of attenuant Mg–Al–Ca–Mn(AXM) system after deserving to compare, or will make industrial level forging alloy (Wroughtalloys) , make its have extraordinary high speed to squeeze a sex (High-speedextrudability) , impressibility of meantime effect sclerosis (Age-hardeningresponse) is splitting also. If can apply its board shape alloy, predict to will produce tremendous effect to automobile industry.
Accordingly, this group ever tried to carry AMX system research and development for many times board shape alloy (Sheetalloys) . Machining Mg–1.1Al–0.3Ca–0.2Mnat. %(atomic per cent) during alloy, its discovery needs only will a few zinc (0.3at. After %) adds Mg–1.1Al–0.3Ca–0.2Mn alloy, will promote its to extend considerably shape function. In addition, the ageing when the course is short (Subsequentshorttimeaging) will bring about intensity of the alloy that contain zinc to appear to promote considerably.
The alloy of new research and development by entitle AXMZ1000, this alloy shapes in what normal temperature falls the aluminium alloy that function can rival moderate strength, latter is used at making car automobile body more. In addition, the intensity of this alloy compares aluminium alloy tall 1.5-2 times.
After mixing a few zinc and magnesian metal to this alloy, will form granule structure (after Finegrainstructures); joins aluminium and calcium, implementation high strenth, group of atom of this profit from forms a cluster (of Atomicclusters) generate, promoted the intensity of alloy then.
The alloy of new research and development all is made by common metal, its cost of material is not costly. Of this alloy make reach heat treatment craft is simple, can be this alloy treatment metallic thin plate, what use technology common also make at aluminium alloy in.